OnFlex™ HT 60A-3S2101
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | OnFlex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xVxWrQ_OnFlex-HT-60A-3S2101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OnFlex™HT thermoplastic elastomer polymer is based on hydrogenated styrene block copolymer. This series of polymers specializes in providing good compression permanent deformation resistance and high heat resistance at high temperatures. In addition, OnFlex™HT polymer conforms to EN 681-2 standard, providing excellent mechanical properties, wide hardness range and good processability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shao A, 3 seconds, 23°C, 6.00mm, injection molding) | 60 | DIN 53505 | |
| IRHD Hardness | 70 | ISO 48 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | DIN 53504 | ||
| Lateral flow : fracture, 23°C, 2.00mm | 10.5 | MPa | DIN 53504 |
| Traffic : fracture, 23°C, 2.00mm | 7.90 | MPa | DIN 53504 |
| Tensile Elongation 2 | DIN 53504 | ||
| Lateral flow : fracture, 23°C, 2.00mm | 840 | % | DIN 53504 |
| Traffic : fracture, 23°C, 2.00mm | 650 | % | DIN 53504 |
| Tear Strength | 32 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| -10°C, 72 hr | 46 | % | ISO 815 |
| 23°C, 22 hr | 24 | % | ISO 815 |
| 70°C, 22 hr | 33 | % | ISO 815 |
| 100°C, 22 hr | 42 | % | ISO 815 |
| 125°C, 22 hr | 43 | % | ISO 815 |
| 150°C, 22 hr | 65 | % | ISO 815 |
| Stress relaxation | ISO 3384 | ||
| 23°C 3 | 13 | % | ISO 3384 |
| 23°C 4 | 31 | % | ISO 3384 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| General Material Type | Styrene thermoplastic elastomers (TES) |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (70°C, 168 hr, 2.00 mm) | -0.50 | % | DIN 53504 |
| Change in Tensile Strain at Break in Air (70°C, 168 hr, 2.00 mm) | -0.90 | % | DIN 53504 |
| Change in Shore Hardness in Air (Support A, 70°C, 168 hr) | -3.0 | DIN 53505 | |
| Change in Volume | ISO 1817 | ||
| 70°C, 72 hr, in ASTM #1 oil | 10 | % | ISO 1817 |
| 70°C, 168 hr, in water | 0.20 | % | ISO 1817 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| 各项属性值是采用注射模制基板测量得出。 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 200 mm/min |
| 2 . | 200 mm/min |
| 3 . | 168 hours, 25% intensity of compression, method A |
| 4 . | 100 days, 25% intensity of compression, method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PEI-GP1-TFE5 | Polymer Resources Ltd. | PEI | PRL |
| RheTech Thermoplastic Polyolefin FT4802-691UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Durepol® PBT A3 G20 BRCA010 BT325 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| LNP™ THERMOCOMP™ IX04513C compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |
| Dow Corning® C6-530 | Dow Corning Corporation | Silicone | Dow Corning® |