Vyncolit® SI 9002N
| Category: | Silicone , Silicone |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xVRaDQ_Vyncolit-SI-9002N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SI 9002N is a short fiberglass reinforced silicone molding compound, which offers moderate strength properties, and dimensional stability and excellent long-term thermal stability at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.90 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (Compression Molded) | 0.50 - 0.80 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.16 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 27.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 14000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 52.0 | MPa | ASTM D790 |
| Compressive Strength | 88.0 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 22 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 282 | °C | ASTM D648 |
| CLTE - Flow | 3.3E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.81 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 9.5 | kV/mm | ASTM D149 |
| -- 2 | 8.8 | kV/mm | ASTM D149 |
| Arc Resistance | 210 | sec | ASTM D495 |
| Additional Information |
|---|
| All ASTM properties listed were tested in accordance with ASTM D5948.The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM C518.Powder Density, ASTM D1895: 0.9 g/cm³Water Absorption, ASTM D570, 48 hrs, 50°C: 0.39%DTUL @264psi - Unannealed, ASTM D648, Post Baked, Compression Molded: >282°CDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 8.8 kV/mmDielectric Strength, ASTM D149, 60 Hz, Method A, wet: 9.5 kV/mm |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ALC-90A | Biomerics, LLC | TPU-PC | Quadrathane™ |
| SUNFROST® KD80MA | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| Advanced Composites ADX-5001 | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Artenius MB01 | Artenius | PET | Artenius |
| Hax™ HFC 087/2 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |