Ultramid® B3ZG8 BK20560
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xUTZgg_Ultramid-B3ZG8-BK20560.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3ZG8 BK20560 is an impact-modified, pigmented black and 40% glass fiber reinforced injection molding PA6 grade having very high impact strength and rigidity. Applications Typical applications include airbag housings and half-shells for suitcases. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/5.0 kg) | 4.00 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.6 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11600 | 6700 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 160 | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 4.0 | 9.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9500 | 6100 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 14 | -- | kJ/m² | |
| 23°C | 22 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 245 to 275 | °C | |
| Middle Temperature | 260 to 285 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® RX®2-501N | Vyncolit N.V. | DAP | Vyncolit® |
| ACCUGUARD™ CP0467V2CSL | ACLO Compounders Inc. | PP Copolymer | ACCUGUARD™ |
| NOVALAC RX®448 | Vyncolit N.V. | Phenolic | NOVALAC |
| Sylvin 8878-80 Brown 7380 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ STAT-KON™ EE005E compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |