AIE LCP L9010F-GF30
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | AIE LCP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xUFqRH_AIE-LCP-L9010F-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AIE LCP L9010F-GF30 is a Liquid Crystal Polymer (LCP) material filled with 30% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of AIE LCP L9010F-GF30: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 to 0.50 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 155 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 15500 | MPa | ISO 178 |
| Flexural Stress 2 | 205 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 15 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 273 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 265 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 to 160 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 300 to 330 | °C | |
| Mold Temperature | 80.0 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | 3.0 mm/min |
| 2 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 7011LT-03 | Colorite Polymers | PVC, Unspecified | Unichem |
| KOPLA PA66 KDG1080 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| INEOS PP H35G-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| Sylvin 86021-70FUV White 1533 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ STAT-KON™ KEP33 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |