LGSTRENE LGG 102
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | LG Polymers India Pvt. Ltd. |
| Trademark: | LGSTRENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xRMknL_LGSTRENE-LGG-102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LGSTRENE LGG 102 is a General Purpose Polystyrene material. It is available in Asia Pacific. Primary attribute of LGSTRENE LGG 102: Flame Rated. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 40.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 3290 | MPa | ASTM D790 |
| Flexural Strength | 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 12 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 81.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMN Y BZ TL | Arkema | Nylon 11 | Rilsan® |
| RTP 201 GB 30 | RTP Company | Nylon 66 | RTP |
| Braskem PE SBC818 | Braskem America Inc. | LDPE | Braskem PE |
| Durez® 13848 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Latamid 66 H2 G/25 | LATI S.p.A. | Nylon 66 | Latamid |