VALOX™ 325F resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xPPZDg_VALOX325Fresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LIMITED USE, PM Approval required. VALOX 325F is compliant with food contact regulations. VALOX 325F is a general purpose, unreinforced PBT injection moulding resin which contains internal mold release. Available in natural colour only (1001). This grade is similar to 325. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Flow | 1.1 - 1.8 | % | Internal method |
| Transverse flow | 0.90 - 1.8 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.34 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 85.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.0 | % | ISO 527-2/50 |
| Fracture | 60 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2300 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 9.00 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 3 | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C 4 | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact 6 | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, unannealed, 100 mm span | 110 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 50.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 220 | °C | ISO 306/A50 |
| -- | 175 | °C | ISO 306/B50, ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.16 | W/m/K | ISO 8302 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 1.00 mm 9 | 16 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | IEC 60250 | |
| 60 Hz | 3.30 | IEC 60250 | |
| 1 MHz | 3.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 2.0E-3 | IEC 60250 | |
| 60 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.0 mm | 850 | °C | IEC 60695-2-12 |
| 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40 - 60 | °C | |
| Rear Temperature | 230 - 245 | °C | |
| Middle Temperature | 240 - 255 | °C | |
| Front Temperature | 245 - 265 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 sp=62mm |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 120*10*4 mm |
| 9 . | Short-Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene HFR8224 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| Tritan™ GX100 | Eastman Chemical Company | Copolyester | Tritan™ |
| ALTECH® PA6 A 4020/100 MR20 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Clariant Nylon 6/6 PA-111G33C | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Devcon Aluminum Liquid (F-2) | Devcon | Epoxy | Devcon |