ELITE™ 5101G
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xOMth8_ELITE-5101G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
ELITE™ 5101G Enhanced Polyethylene Resin is a copolymer produced via INSIT™ Technology from Dow Plastics. It offers extremely high impact resistance, combined with good tear and tensile properties. In addition, this resin exhibits higher hot tack strength than LLDPE for automated packaging applications. |
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Energy (51 µm) | 4.29 | J | Internal method |
| Film Puncture Force (51 µm) | 71.2 | N | Internal method |
| Film Puncture Resistance (51 µm) | 11.0 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 219 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 248 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 9.79 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 11.0 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 40.8 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 38.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 590 | % | ASTM D882 |
| TD : Fracture, 51 µm | 620 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | > 850 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 720 | g | ASTM D1922 |
| TD : 51 µm | 1000 | g | ASTM D1922 |
| Seal Initiation Temperature 1(51 µm) | 106 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 121 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 58 | ASTM D2457 | |
| Haze (50.8 µm) | 15 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 232 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：单跨双混合 模具间隙：70 密尔 (1.8 mm) 熔体温度： 450°F (232°C) 输出：模具周长的 6 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：78 rpm 冷冻线高度：25 英寸 (635 mm) |
| Note Message | |
|---|---|
| 1 . | Achieve a temperature of 2 psig (8.8 N/25.4mm) heat seal strength. Heat seal strength, Topwave HT tester 0.5 S holding pressure, 40 psi pressure, pulling speed 10 inches/min (250 mm/s). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AMTOPP AF30 | Inteplast Group | PP, Unspecified | AMTOPP |
| Fortron® MT9320C0 | Celanese Corporation | PPS | Fortron® |
| EOS PA 1101 | EOS GmbH | Nylon 11 | EOS |
| Sylvin 9772-75 Grey 9222 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9077-90LMW Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |