Bayflex® 906 (34 pcf)
| Category: | PUR-MDI , Polyurethane (MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xNgBl4_Bayflex-906-34-pcf-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bayflex 906 is a fully compounded, water-blown, polyether-based polyurethane system consisting of two liquid components. Component A is a modified diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. Bayflex 906 system was developed for use in a wide variety of applications requiring a microcellular core and a tough, abrasion-resistant outer surface. Examples of possible applications include appliance handles, office chair armrests, and dunnage strips. As with any product, use of the Bayflex 906 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shaw A, 12.7mm) | 75 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 12.7 mm) | 5.65 | MPa | ASTM D412 |
| Tensile Elongation (Break, 12.7 mm) | 200 | % | ASTM D412 |
| Tear Strength 1(12.7 mm) | 27.5 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components 2 | |||
| Component a | Mixing ratio by weight: 73 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information |
|---|
| Part A Type: Isocyanate Specific Gravity @ 25°C: 1.21 Viscosity @25°C: 800 mPa Flash Point, PMCC: 213°C NCO: 22.6 to 23.1 wt% Part B Type: Polyol Specific Gravity @ 25°C: 1.02 Viscosity @25°C: 1100 mPa-s Flash Point, PMCC: 121°C Water: 0.60 wt% max Hydroxyl Number: 194: mg KOH/g Material Temperatures: 25 to 40°CMold Temperature: 55 to 65°CDemold Time, 0.25 in thickness: 3.5 minLinear Shrinkage at 0.50 g/cm³: <0.5%Hand Mix Reactivity at 23°C Cream Time: 50 sec Tack-Free Time: 60 sec Pull Time: 90 sec Free-Rise Density: 11 to 16 lb/ft³ |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 98 Index |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SumiDurez 115 | SumiDurez Singapore Pte Ltd | Phenolic | SumiDurez |
| Fainplast PVC PM 6510 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Magnobond 6398 | Magnolia Plastics, Inc. | Epoxy | Magnobond |
| Sylvin 4200-88 Clear Green 3210 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 2990-82 Clear 8463 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |