HOPELEX AG-3020
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HOPELEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xM8nki_HOPELEX-AG-3020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS with balanced flowability, impact properties and hydrolytic stability |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 56.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 80 | % | ASTM D638 |
| Flexural Modulus 3 | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(Yield) | 86.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 98 | J/m | |
| 23°C, 3.18 mm | 540 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 95.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 3405 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Chemical Resources SAN2000 | Chemical Resources, Inc. | SAN | Chemical Resources |
| Hanwha Total PP HF429 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Homopolymer | Hanwha Total PP |
| Jam HDPE HM9455F1 | Jam Petrochemical Company | HDPE | Jam HDPE |
| Ultramid® Structure A3WG12 LFX BK23215 | BASF Corporation | Nylon 66 | Ultramid® |