Order Products : sales@su-jiao.com
HiPrene® MT42
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GS Caltex |
| Trademark: | HiPrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xLAlV7_HiPrene-MT42.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiPrene® MT42 is a medium melt flow, 20% mineral filled polypropylene compound. This material has good flowability and it is easy to process. Because of it's good impact/stiffness balance is suitable for Industrial Parts and non-visible automotive interior parts.This grade is available in natural or color-matched, pellet form. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 10 | g/10 min | ASTM D1238 |
| Ash Content (600°C) | 20 | % | Internal method |
| Volatile Matter | 0.10 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 27.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus 1(23°C) | 2700 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 6.00 | kJ/m² | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 4.00 - 6.50 | MPa |
| Injection instructions |
|---|
| Back Pressure: Low to MediumScrew Speed: Low to MediumInjection Speed: 100 to 200 m/min |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-2430 | Quantum Composites Inc. | Phenolic | Quantum Composites |
| Restren ABS | Polimarky Spolka Jawna | ABS | Restren |
| TORZEN® U4800 NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Elastron® G G500.A70.N.PA | Elastron USA, Inc. | SEBS | Elastron® G |
| Lusin® Clean 1500 | Chem-Trend L.P. | Unspecified | Lusin® |