Glass-fibre reinforced phenolic moulding compound Exceptional heat resistance with regard to maintaining surface finish and mechanical properties, outstanding mechanical properties, excellent rotational symmetry This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 to 1.80 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.90 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.30 to 0.50 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.20 | % | ISO 62 |
| Post Shrinkage 2 | < 0.20 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 8000 to 10000 | MPa | ISO 527-2 |
| Tensile Stress (Compression Molded) | 50.0 to 70.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 11000 to 14000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 80.0 to 100 | MPa | ISO 178 |
| Compressive Stress | 200 to 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 2.0 to 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (Compression Molded) | 6.0 to 9.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 180 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 160 to 180 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 150°C) | 1.5E-5 to 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.40 to 0.60 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 to 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 20 to 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 8.00 6.00 | ||
| 1 MHz | 6.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.10 to 0.20 | ||
| 1 MHz | 0.020 to 0.030 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | > 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Tested by Synres-Almoco) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 LF | RTP Company | PEEK | RTP |
| Milastomer™ 9070NS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Toughblend® PC-1400 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC | Toughblend® |
| TUFNYL® RXXIN NATURAL | SRF Ltd. | Nylon 66 | TUFNYL® |
| Globalprene® 3501P | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |