SABIC® PP QR6711K

Category:	PP Random Copolymer , Polypropylene Random Copolymer
Manufacturer:	SABIC Americas, Inc.
Trademark:	SABIC® PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	xHmu1n_SABIC-PP-QR6711K.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Provisional - PP random co-polymer for Injection moulding

QR6711K is a controlled Rheology grade with narrow molecular weight distribution intended specifically for producing injection molded articles with high clarity, good flow properties & better impact properties than homo PP counterparts. This grade contains advance clarifier & anti-static agent.

QR6711K has following features:

Consistent processability

Good stiffness

Exceptional clarity

Low thickness

Low warpage

Easy to flow

Better cycle time comparing to normal random grades

Less energy consumption

Typical Applications
QR6711K can be used mainly for clear thin wall containers & boxes, housewares, caps & closures and lids.

General Information
Additive	Antistatic Clarifier
Features	Antistatic Controlled Rheology Fast Molding Cycle Food Contact Acceptable Good Flow Good Impact Resistance Good Processability Good Stiffness High Clarity Low Warpage Narrow Molecular Weight Distribution Random Copolymer
Uses	Caps Closures Household Goods Lids Thin-walled Parts Transparent Parts
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity ¹	0.905	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	45	g/10 min	ASTM D1238
Molding Shrinkage - Flow	1.0 to 2.0	%

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale, Injection Molded)	85		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield, Injection Molded)	28.0	MPa	ASTM D638
Tensile Elongation (Yield, Injection Molded)	13	%	ASTM D638
Flexural Modulus - 1% Secant (Injection Molded)	1150	MPa	ASTM D790A

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, Injection Molded)	56	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	71.0	°C	ASTM D648
Vicat Softening Temperature	124	°C	ASTM D1525 ²

Injection	Nominal Value	Unit
Rear Temperature	185 to 225	°C
Middle Temperature	185 to 225	°C
Front Temperature	185 to 225	°C
Mold Temperature	25.0 to 40.0	°C

Note Message
1 .	23°C
2 .	Rate B (120°C/h)

Resin Grade	Manufacturer	Category	Trademark
ULTEM™ ATX200F resin	SABIC Innovative Plastics	PEI+PCE	ULTEM™
ACCUCOMP™ CP0408L	ACLO Compounders Inc.	PP Copolymer	ACCUCOMP™
Andur AL 90 AP/Curene® 89LC	Anderson Development Company	PUR-Eth,aliphat	Andur
ATPioneers PP CAP501	Asia Technology Pioneers Ltd	TPO	ATPioneers PP
ESPRENE EPDM 606F	Sumitomo Chemical Co., Ltd.	EPDM	ESPRENE EPDM