Resilience™ HC 4895
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Resilience™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xGnf98_Resilience-HC-4895.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Resilience™ HC 4895 is a Rigid Polyvinyl Chloride product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Medical/Healthcare. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Spiral Flow | 88.9 | cm | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2410 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 42.7 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 58 | % | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| 0°C, 3.18 mm, Injection Molded | 590 | J/m | |
| 23°C, 3.18 mm, Injection Molded | 910 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 71.1 | °C | |
| 0.45 MPa, Annealed, 6.35 mm | 73.9 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 67.8 | °C | |
| 1.8 MPa, Annealed, 6.35 mm | 72.2 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Transparents) | V-0 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3180 µm) | 79.0 | % | ASTM D1003 |
| Haze (3180 µm) | 8.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 199 to 204 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LP 129/2 GL | A. Schulman Europe | ABS | POLYMAN® |
| TECHNYL STAR™ SX 216 V60 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| Axiall PVC 11441 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Jampilen RP316M | Jam Polypropylene Company | PP Random Copolymer | Jampilen |
| Braskem PP DR155.01 | Braskem Europe GmbH | PP Random Copolymer | Braskem PP |