Veradel® AG-320

Category:	PESU , Polyethersulfone
Manufacturer:	Solvay Specialty Polymers
Trademark:	Veradel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	xGdNbg_Veradel-AG-320.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Veradel® AG-320 is a 20% glass fiber reinforced grade of polyethersulfone (PESU). Adding glass fiber to polyethersulfone substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the material, while maintaining most of its other basic characteristics. The combination of structural properties and cost effectiveness make this resin an attractive alternative to metals in many engineering applications.

This grade was formerly marketed as Radel® A PESU

Natural: Veradel® AG-320 NT

General Information
Filler / Reinforcement	Glass Fiber, 20% Filler by Weight
Features	Acid Resistant Flame Retardant Food Contact Acceptable Good Adhesion Good Chemical Resistance Good Creep Resistance Good Dimensional Stability Good Strength Good Thermal Stability Good Toughness High Heat Resistance High Rigidity High Tensile Strength Hydrolysis Resistant Medium Flow Medium Molecular Weight
Uses	Appliance Components Appliances Automotive Electronics Batteries Business Equipment Electrical Parts Electrical/Electronic Applications Food Service Applications Industrial Applications Metal Replacement Microwave Cookware Plumbing Parts Valves/Valve Parts
Agency Ratings	NSF 51 3
RoHS Compliance	RoHS Compliant
Appearance	Colors Available Natural Color
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.51	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (343°C/2.16 kg)	6.0	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.40	%	ASTM D955
Water Absorption (24 hr)	0.45	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	5690	MPa	ASTM D638
Tensile Strength (Yield)	109	MPa	ASTM D638
Tensile Elongation (Break)	3.2	%	ASTM D638
Flexural Modulus	6550	MPa	ASTM D790
Flexural Strength	162	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	59	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm)	214	°C	ASTM D648
CLTE - Flow (3.18 mm)	3.1E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	> 1.0E+16	ohms·cm	ASTM D257
Dielectric Strength	17	kV/mm	ASTM D149
Dielectric Constant			ASTM D150
60 Hz	3.84
1 kHz	3.84
1 MHz	3.88
Dissipation Factor			ASTM D150
60 Hz	1.5E-3
1 kHz	1.8E-3
1 MHz	8.1E-3

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹(0.787 mm)	V-0		UL 94

Injection	Nominal Value	Unit
Drying Temperature	149 to 177	°C
Drying Time	2.5 to 4.0	hr
Processing (Melt) Temp	343 to 399	°C
Mold Temperature	149 to 163	°C
Injection Rate	Fast
Back Pressure	0.345 to 0.689	MPa
Screw Compression Ratio	2.0:1.0

Note Message
1 .	These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions.

Resin Grade	Manufacturer	Category	Trademark
Maxxam™ PPR-40G Black	PolyOne Corporation	PP Homopolymer	Maxxam™
TOTAL Polypropylene PPH 3860X	TOTAL Refining & Chemicals	PP Homopolymer	TOTAL Polypropylene
CYCOM® 2020	Cytec Industries Inc.	Epoxy	CYCOM®
Grilamid® 2D 25 W 20 HL X black 9992	EMS-GRIVORY	Nylon 6/12	Grilamid®
INCOLOR PP BK002	Infinity LTL Engineered Compounds	PP Homopolymer	INCOLOR