MAJ'ECO FP364M - 8717
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xFyTI1_MAJ-ECO-FP364M---8717.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO FP364M - 8717 is a vegetal fibre polypropylene compound intended for injection moulding. MAJ'ECO FP364M - 8717 has been developed especially for demanding applications in various engineering sectors. APPLICATIONS Product such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.4 - 1.6 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3860 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 3180 | MPa | ISO 178 |
| Flexural Stress | 61.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 109 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 150 - 190 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2700 S-60A MD NATURAL | RTP Company | SEBS | RTP |
| Visico™ LE4421/LE4460/ LE4437 | Borealis AG | PE, Unspecified | Visico™ |
| APEX® 310 | Teknor Apex Company | PVC, Flexible | APEX® |
| Geon™ Vinyl Flexible B8502 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Karina BLACK PVC COMPOUND TR-781-48/1-B-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |