| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Cevian®-V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xEsVzh_Cevian--V-320-320SF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cevian®-V 320, 320SF is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific. Primary attribute of Cevian®-V 320, 320SF: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 43.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 17 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 150 | J/m | |
| 23°C, 6.40 mm | 300 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 87.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 77.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Ball Pressure Test | 90 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 to 3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Screw Speed | 70 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 613TIC | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| NYCOA Polyamide 5201 HS | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| Dynalloy™ OBC 8100-N75 | PolyOne Corporation | TPE | Dynalloy™ |
| INSPIRE™ 6021N | Braskem America Inc. | PP Homopolymer | INSPIRE™ |
| Paracril® CLT | INSA | NBR | Paracril® |