Lupoy® GP5006AF
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xEU8am_Lupoy-GP5006AF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Flame Retardant Application Elecric and Electronic Housing and Components |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 5.0 to 8.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 51.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 60 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2160 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 104 | °C | ASTM D648 |
| RTI Elec | UL 746 | ||
| -- | 60.0 | °C | |
| 0.750 mm | 85.0 | °C | |
| 1.70 mm | 85.0 | °C | |
| 3.00 mm | 85.0 | °C | |
| RTI Imp | UL 746 | ||
| -- | 60.0 | °C | |
| 0.750 mm | 75.0 | °C | |
| 1.70 mm | 75.0 | °C | |
| 3.00 mm | 75.0 | °C | |
| RTI Str | UL 746 | ||
| -- | 60.0 | °C | |
| 0.750 mm | 75.0 | °C | |
| 1.70 mm | 75.0 | °C | |
| 3.00 mm | 75.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 34 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 9.0E-3 | ASTM D150 | |
| Arc Resistance (1.59 mm) | 100 | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.70 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| High Voltage Arc Resistance to Ignition (HVAR) (3.00 mm) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.70 mm | PLC 3 | ||
| 3.00 mm | PLC 2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.70 mm | V-0 | ||
| 3.00 mm | V-0 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 245 to 275 | °C | |
| Front Temperature | 245 to 275 | °C | |
| Nozzle Temperature | 245 to 275 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 GF 30 S1 black (1281) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| APEX® 94-A0098C-50 | Teknor Apex Company | PVC, Flexible | APEX® |
| extrufib® 8020 | Technamation Technical Europe GmbH | PP, Unspecified | extrufib® |
| Hostacom EKC 265N G51359 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ LUBRILOY™ KL201 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRILOY™ |