Duron PEI 5001
| Category: | PEI , Polyether Imide |
| Manufacturer: | ProPolymers Inc. |
| Trademark: | Duron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xEGsKA_Duron-PEI-5001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Duron PEI 5001 is a polyetherimide copolymer that offers very good chemical resistance compared to our PEI 1000 resin. It has a superior combination of mechanical, electrical, and thermal properties. PEI is inherently flame resistant with low smoke emission. It also has better ductility and processability than PEI 1000. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 4.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18mm | 0.40 - 0.70 | % | ASTM D955 |
| Transverse flow : 3.18mm | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.16 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 100 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 8.0 | % | ASTM D638 |
| Fracture | 70 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 204 | °C | ASTM D648 |
| Vicat Softening Temperature | 219 | °C | ASTM D1525 |
| CLTE - Flow | 5.5E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256: 8 kJ/m²Unnotched Izod Impact, ASTM D256: No Break kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF4CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Triapol® Blends C3 K46 NTLA010 BS308 | Petropol Industry and Trade of Polymers LTDA | PC+ABS | Triapol® Blends |
| ACCULOY™ PCS003L | ACLO Compounders Inc. | ASA+PC | ACCULOY™ |
| LOXIM 230 12 HB | LOXIM Industries Private Limited | PBT | LOXIM |
| Lupolen 2427 H | LyondellBasell Industries | LDPE | Lupolen |