INEOS PP H02C-04
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xDyeBb_INEOS-PP-H02C-04.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| H02C-04 is a low flow rate, high clarity, nucleated homopolymer designed for extrusion, thermoforming, blow molding and rigid packaging applications that require good see-through clarity combined with good heat resistance. H02C-04 utilizes new nucleator technology that gives the finished part a slight bluish hue resulting in a clearer and crisper-looking final product. Typical applications include thermoformed cups, containers and lidding; extrusion blow molded containers and bottles, injection stretch blow molded containers and bottles and extruded sheets and profiles. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.909 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.3 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 36.5 | MPa | |
| Break | 18.6 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 9.7 | % | |
| Break | 100 | % | |
| Flexural Modulus - 1% Secant | 1610 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Notched Izod Impact (Area) (23°C) | 6.50 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 95 | ASTM D2457 | |
| Haze 3(1270 µm) | 31 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 6594N-WGL65 | TSRC Corporation | SEBS | T-Blend® |
| 4PROP® 9C21120 FR5 | 4Plas | PP Copolymer | 4PROP® |
| K-PU 7760 | Technovinyl Polymers India Ltd. | TPU, Unspecified | K-PU |
| Lumid庐 GP2151BF | LG Chem Ltd. | Nylon 66 | Lumid® |
| Sylvin 916VO Grey 992 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |