Moplen HP561R

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	LyondellBasell Industries
Trademark:	Moplen
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	xCmdg8_MoplenHP561R.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Homopolymer Resin for Spunbond Fiber

Features:

High melt flow with very narrow MWD resin for high speed spin continuity of low denier fiber

Very uniform melt flow rate and low gel

Excellent processability and wide processing operating window

Spinnability improved with enchanted fabric properties

Very good gas fading resistance

Applications:

Spunbonded nonwoven fabric using for hygine products, medical, agriculture, geotextile, etc.

General Information
Additive	Anti-smoke fade
Features	Low speed solidification crystal point Homopolymer Resistance to gas fading Workability, good High liquidity Narrow molecular weight distribution
Uses	Spunbond nonwoven fabric Fiber
Processing Method	Fiber (spinning) extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.900	g/cm³	ASTM D792B
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	25	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	32.0	MPa	ASTM D638
Tensile Elongation (Yield)	11	%	ASTM D638
Flexural Modulus	1240	MPa	ASTM D790A

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	24	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	94.0	°C	ASTM D648

Resin Grade	Manufacturer	Category	Trademark
Witcom PP 2012/078 Blue	Witcom Engineering Plastics B.V.	PP, Unspecified	Witcom PP
BMC 902	Bulk Molding Compounds, Inc.	Polyester, TS	BMC
DIGITALWAX® DC 500	DWS Systems	Unspecified	DIGITALWAX®
LNP™ STAT-KON™ EX12406C compound	SABIC Innovative Plastics	PEI	LNP™ STAT-KON™
LG ASA LI980	LG Chem Ltd.	ASA	LG ASA