Sumikon® PM-6630 (Type: Black)
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xBdgBB_SumikonPM6630TypeBlack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON PM-6630 Type Black is a Short Glass fiber & Mineral molding compound based on Phenolic Novolac polymer. It is supplied in the form of Granular/Molding Powder for Molding. This grade is official registered UL with V-0 (t=3.0). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.78 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.18 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 122 | MPa | JIS K6911 |
| Flexural Modulus | 18300 | MPa | JIS K6911 |
| Flexural Strength | 228 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.7 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 231 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | JIS K6911 | ||
| -- 1 | 3.0E+12 | ohms | JIS K6911 |
| -- 2 | 5.0E+11 | ohms | JIS K6911 |
| Note Message | |
|---|---|
| 1 . | As molded |
| 2 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 407 | RTP Company | PS (GPPS) | RTP |
| Scolefin 42 T 23-0 | Ravago Group | PP Copolymer | Scolefin |
| ULTEM™ 1000 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| PENTAMID A GV30 HYD schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| ESTOPLAST XU 6100BL17 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |