LNP™ THERMOCOMP™ UX06032 compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xAI1vc_LNP-THERMOCOMP-UX06032-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* UX06032 is a compound based on Polyphthalamide resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Non-Brominated & Non-Chlorinated Flame Retardant, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound UX06032-BK83015 Product reorder name: UX06032 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.20 to 0.30 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.23 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 9900 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 275 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 258 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.1E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 825 | °C | |
| 1.60 mm | 825 | °C | |
| 3.00 mm | 850 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 290 to 310 | °C | |
| Front Temperature | 295 to 315 | °C | |
| Processing (Melt) Temp | 305 to 315 | °C | |
| Mold Temperature | 130 to 150 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 83MF90 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| SUMILITE® CEL-4361 | Sumitomo Bakelite Co., Ltd. | LLDPE | SUMILITE® |
| Aurora PVC AP1211 Series | Aurora Plastics, Inc. | PMMA+PVC | Aurora PVC |
| Sylvin 8250-75UV White 1575 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9600-90 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |