TYRIL* styrene-acrylonitrile (SAN) resins are designed to offer superior chemical resistance, strength, hardness and dimensional stability in a broad range of product applications. The key property of TYRIL 867 E is excellent balance of physical properties. TYRIL 867 E is specifically designed to provide good processability, good chemical and heat resistance and very good strength. The UV-stabilized version exhibits excellent weather ability, suitable in particular for extruded sheet and thermoforming applications. Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792, ISO 1183/B |
| -- | 1080 | kg/m³ | ISO 1183 1 |
| Apparent Density | 0.69 | g/cm³ | ASTM D1895, ISO 60 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 220°C/10.0 kg | 12 | g/10 min | |
| 230°C/3.8 kg | 4.0 | g/10 min | |
| Melt volume-flow rate (220°C/10.0 kg) | 14.0 | cm³/10min | ISO 1133 2 |
| Water Absorption | ISO 62 3 | ||
| Saturation | 0.10 | % | |
| Equilibrium | 0.50 | % | |
| Viscosity number | 121 | cm³/g | ISO 307, 1157, 1628 4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 83 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3700 | MPa | ASTM D638, ISO 527-2 |
| Tensile Stress | |||
| Yield | 72.0 | MPa | ISO 527-2 5 |
| Break 6 | 70.0 | MPa | ASTM D638 |
| Break | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 2.6 | % | ISO 527-2 7 |
| Nominal strain at break | 2.6 | % | ISO 527-2 8 |
| Flexural Strength | 97.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | |||
| 23°C | 17 | kJ/m² | ISO 179 |
| -30°C | 18.0 | kJ/m² | ISO 179/1eU 9 |
| 23°C | 17.0 | kJ/m² | ISO 179/1eU 10 |
| Unnotched Izod Impact Strength (23°C) | 14 | kJ/m² | ISO 180 |
| Tensile notched impact strength (23°C) | 19.0 | kJ/m² | ISO 8256/1 11 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 101 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 101 | °C | ASTM D1525, ISO 306/B50 5 12 |
| -- | 110 | °C | ASTM D1525, ISO 306/A120 6 13 |
| 50°C/h, B (50N) | 104 | °C | ISO 306 14 |
| CLTE | |||
| Flow | 5.0E-5 | cm/cm/°C | DIN 53752, ISO 11359-2 15 |
| Transverse | 6.0E-5 | cm/cm/°C | ISO 11359-2 16 |
| Specific Heat | 1380 | J/kg/°C | ASTM D2766 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 17 |
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 18 |
| Electric Strength | 9.1 | kV/mm | IEC 60243-1 |
| Relative Permittivity | |||
| 1 MHz | 3.00 | IEC 60250 | |
| 100 Hz | 3.00 | IEC 60250 19 | |
| Dissipation Factor (1 MHz) | 1.0E-4 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 20(1.60 mm) | HB | UL 94 | |
| Burning Behav. at 1.6mm nom. thickn. (1.50 mm, UL) | HB | ISO 1210 21 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | 5.0 mm/min |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Rate A (50°C/h), Loading 2 (50 N) |
| 13 . | Rate B (120°C/h), Loading 1 (10 N) |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 30 HI K1871 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| SIVIC® E 8610 | SIDIAC | NBR | SIVIC® |
| ADLAS® N09FJB-00 | A.D. Compound S.p.A. | PP Homopolymer | ADLAS® |
| Sarlink® TPE EE-1185B (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| LEXAN™ CFR7630 resin | SABIC Innovative Plastics | PC | LEXAN™ |