LUVOCOM®94-8839 is a low density polyethylene material, which contains a steel filler. This product is available in Europe,. LUVOCOM®The main features of 94-8839 are: Conductivity Electrostatic protection Typical application areas include: engineering/industrial accessories textile/fiber Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Steel filler
Features	Conductivity Electrostatic discharge protection
Uses	Thin wall parts Textile applications Engineering accessories Application in Automobile Field Business equipment
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.20	g/cm³	ISO 1183
Molding Shrinkage	1.0 - 1.6	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	48		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	400	MPa	ISO 527-2
Tensile Stress (Break)	10.0	MPa	ISO 527-2
Tensile Strain (Yield)	20	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	80	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	70.0	°C	UL 746B
Maximum operating temperature- Short Term	110	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	1.0	ohms	IEC 60167

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	80.0	°C	ISO 306/A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 3.2	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature	85.0	°C
Drying Time	2.0 - 3.0	hr
Rear Temperature	160 - 200	°C
Middle Temperature	170 - 220	°C
Front Temperature	180 - 240	°C
Nozzle Temperature	190 - 250	°C
Processing (Melt) Temp	230	°C
Mold Temperature	30.0 - 80.0	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information If originally sealed containers are used, it is normally possible to omit the predrying stage. If PTFE materials are not predried, an increase in deposits inside the mould may occur. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information If originally sealed containers are used, it is normally possible to omit the predrying stage. If PTFE materials are not predried, an increase in deposits inside the mould may occur. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	LDPE , Low Density Polyethylene
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	x93gLp_LUVOCOM-94-8839.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Quadrathane™ ARC-85A	Biomerics, LLC	TPU-PC	Quadrathane™
Uniflon HIPERCONDUX 9 - GMP	UNIFLON	PTFE	Uniflon
APEX® 65012	Teknor Apex Company	PVC, Flexible	APEX®
Jam PE 22501	Jam Petrochemical Company	LLDPE	Jam PE
POCAN® B 3217 XF 000000	LANXESS GmbH	PBT	POCAN®