PALMID® R 6 S GF 10 MV 20 Datasheet,Nylon 6,pal plast GmbH-SHANGHAI SUSHENG

Message
PALMID®R 6 S GF 10 MV 20 is a polyamide 6 (nylon 6) product, which contains 10% glass fiber reinforced materials and 20% mineral fillers. It can be processed by injection molding and is available in Europe. Typical application areas are: housing. Features include: flame retardant/rated flame anti-warping Good dimensional stability Good stiffness

General Information
Filler / Reinforcement	Glass fiber reinforced material, 10% filler by weight Mineral filler, 20% filler by weight
Features	Good dimensional stability Low warpage Rigid, good
Uses	Shell
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.35	g/cm³	ISO 1183
Water Absorption			ISO 62
Saturated, 23°C	6.2	%	ISO 62
Equilibrium, 23°C, 50% RH	1.7	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	6050	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	110	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	3.5	%	ISO 527-2/1A/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	5.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	35	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	207	°C	ISO 306/B50
Melting Temperature (DSC)	220	°C	ISO 3146

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 5800 to 6300 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 100 to 120 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 3 to 4 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 30 to 40 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 4 to 6 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 205 to 209 °CDensity, ISO 1183: 1.34 to 1.36 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 6.1 to 6.3 %Moisture Absorption, ISO 62, 23°C, 50% RH: 1.6 to 1.8 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 5800 to 6300 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 100 to 120 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 3 to 4 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 30 to 40 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 4 to 6 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 205 to 209 °CDensity, ISO 1183: 1.34 to 1.36 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 6.1 to 6.3 %Moisture Absorption, ISO 62, 23°C, 50% RH: 1.6 to 1.8 %

Resin Grade	Manufacturer	Category	Trademark
Small Boss SPVC8014	Tongxiang Small Boss Special Plastic Products Co., Ltd.	PVC, Unspecified	Small Boss
TEREZ PA 6.6 HT 7500 GF 50	TER HELL PLASTIC GMBH	Nylon 66	TEREZ PA 6.6
EGYPTENE HD 6070 UA	Sidpec (Sidi Kerir Petrochemicals Co.)	HDPE	EGYPTENE
HiFill® HDPE TM25	Techmer Engineered Solutions	HDPE	HiFill®
LOTTMER SE-140AB	Lotte Chemical Corporation	SEBS	LOTTMER

Category:	Nylon 6 , Polyamide 6
Manufacturer:	pal plast GmbH
Trademark:	PALMID®
Fillers:	-