REPOL® H026SG
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x4q3u1_REPOL-H026SG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
REPOL Polypropylene H026SG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific catalyst system. Repol H026SG is recommended for Raffia Tapes used in making fabrics for big bags / FIBCs, geotextiles, carpet backing and ropes. Repol H026SG combines good processability on water bath and chill-roll with excellent mechanical properties. Formulated for low water carry-over. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.6 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 34.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 10 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Injection Molded) | 1700 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Peak Melting Temperature 3 | 166 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Second Heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V936 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TPUCO® TPUE-UE95 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Clariant Nylon 6/6 PA-111G20 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Dynacom XAR187 | Dynachem Co. Ltd. | ASA | Dynacom |
| Karina BLACK PVC COMPOUND TR-781-48/1-B-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |