SCHULAMID® 6 MV 14
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x4KLzv_SCHULAMID-6-MV-14.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity Polyamide 6 |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2900 | 1100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 80.0 | 45.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.0 | 20 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 10 | > 100 | % | ISO 527-2/1A/50 |
| Flexural Modulus | 2300 | -- | MPa | ISO 178 |
| Flexural Stress | 100 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 6.5 | -- | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | -- | kJ/m² | |
| 23°C | 7.0 | 50 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 170 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 210 | -- | °C | ISO 306/A50 |
| -- | 190 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 100 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | -- | 850 | °C | |
| 3.00 mm | -- | 850 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoMid B500 | TechnoCompound GmbH | Nylon 6 | TechnoMid |
| TAROLON 2500 G4 X1 | Taro Plast S.p.A. | PC | TAROLON |
| Karina BEIGE PVC COMPOUND 800-08/52-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupox® HI2100M | LG Chem Ltd. | PBT | Lupox® |
| SHINSTRA WG35TKB | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |