TOTAL Polypropylene PPH 3485WZ

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	TOTAL Refining & Chemicals
Trademark:	TOTAL Polypropylene
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	x22E55_TOTALPolypropylenePPH3485WZ.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene 3485WZ produces thermoformed parts with good clarity, gloss and sidewall stiffness.

High Purity: 3485WZ features minimum taste and odor and optimum thermal stability for superior color and processability.

FDA: 3485WZ complies with all applicable FDA regulations and may be used under these provisions for food contact and packaging.

Applications: 3485WZ is ideal for deli containers, drinking cups, lids, and food service trays.

Processing: 3485WZ resin processes on in-line, narrow web thermoforming and solid phase pressure forming equipment with typical melt temperature at 450°-500°F (232-260°C).

General Information
Features	Good Clarity Good Gloss High purity Rigid, good Homopolymer Workability, good The smell is low to none The smell is low to none Thermal stability, good Compliance of Food Exposure
Uses	Thermoforming Applications Cup Cover Sheet Food packaging Food service sector Food container
Agency Ratings	FDA Food Exposure, Not Rated
Forms	Particle
Processing Method	Sheet extrusion molding Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	4.1	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1930	MPa	ASTM D638
Tensile Strength	38.6	MPa	ASTM D638
Tensile Elongation (Break)	5.7	%	ASTM D638
Flexural Modulus	1860	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	43	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	111	°C	ASTM D648
Melting Temperature	166	°C	DSC

Optical	Nominal Value	Unit	Test Method
Haze (508 µm)	20	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	232 - 260	°C

Resin Grade	Manufacturer	Category	Trademark
PrimaFlex® GP 0900	Plastic Solutions, Inc.	PS (GPPS)	PrimaFlex®
THERMOLAST® K TF9CGN (Series: FC)	KRAIBURG TPE	TPE	THERMOLAST® K
Ultradur® B 4520	BASF Corporation	PBT	Ultradur®
Haysite Plastics HTF	Haysite Reinforced Plastics	Polyester, TS	Haysite Plastics
SIBUR Synthetic Rubber IR SKI-3 NST Group I	SIBUR	IR	SIBUR Synthetic Rubber