Osterlene® HIPS2.63.6
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Osterman & Company |
| Trademark: | Osterlene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x1UtVI_OsterleneHIPS2636.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.6 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2210 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 28.3 | MPa | ASTM D638 |
| Flexural Modulus 3(50.8mm span) | 2130 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.8 mm Span) | 42.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Annealed, 3.18 mm) | 90.6 | °C | ASTM D648 |
| Vicat Softening Temperature | 92.2 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | Type 1, 51mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 FR UV | RTP Company | Nylon 66 | RTP |
| TOTAL Polypropylene Lumicene® M 6823 MZ | TOTAL Refining & Chemicals | PP Copolymer | TOTAL Polypropylene |
| Anjacom® J255-H/GF30 | Almaak International GmbH | Nylon 6 | Anjacom® |
| Guang Sung PVC GPMA80T | Guang Sung Plastics (GSPL) | PVC, Unspecified | Guang Sung PVC |
| LNP™ LUBRILOY™ RX05497 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |