OPNYL OP66UT 119
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | OPNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x0gQwF_OPNYL-OP66UT-119.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultra Tough - High Impact, Excellent retention of mechanical properties, High service temperature. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.17 mm | 1.1 to 1.3 | % | |
| Across Flow : 3.17 mm | 1.5 to 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1700 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 51.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 130 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 1800 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 73.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 420 | J/m | |
| 23°C | 950 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 210 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 63.0 | °C | |
| Peak Melting Temperature | 256 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIVIC® 8010 | SIDIAC | NBR | SIVIC® |
| Alkathene® LDF433AB | Qenos Pty Ltd | LLDPE | Alkathene® |
| Exxtral™ Performance Polyolefin CMU101 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Karina CLEAR PVC COMPOUND 80/229-IS-RG-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| HyFlex P021 | KMI Group, Inc. | Copolyester | HyFlex |