UNIVAL™ DMDA-6147 NT 7 High Density Polyethylene (HDPE) Resin is a polymer with broad molecular weight distribution and high molecular weight. This product provides an excellent combination of extrudability and parison stability, which contribute to uniform wall thickness in large parts. UNIVAL DMDA-6147 NT 7 HDPE resin is ideal for blow molding containers such as the 5-55 gallon (19-212 liter) closed head shipping containers and other similar parts. The broad distribution also provides outstanding environmental stress crack resistance (ESCR) at a good rigidity. Because of these characteristics, a wide variety of products, such as industrial chemicals, latex paints, printing inks, foodstuffs, adhesives, and other chemical specialties may be packaged in containers produced from this resin. The smooth surface of molded parts is readily treated and printed for high quality applications. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 10 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | > 1500 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 22.8 | MPa | ASTM D638 |
| Fracture | 36.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | ASTM D638 |
| Fracture | 900 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 855 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 462 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 66.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 130 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 114 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8802 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Unichem 89-379DL-30 | Colorite Polymers | PVC, Flexible | Unichem |
| NILFLEX® 14 K15TE | Taro Plast S.p.A. | PP Copolymer | NILFLEX® |
| Rotuba CAP CP808 (13% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |
| XYLEX™ X7507 resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |