Next Nylon 66 Prime Series PG50-01NC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wzfDl1_Next-Nylon-66-Prime-Series-PG50-01NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass Fiber Reinforced Natural Compound Product Applications Typical Applications include Industrial articles having very high rigidity Benefits Where a balance of continuous heat and peak temperature property retention is needed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.57 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.30 | -- | % | ASTM D955 |
| Transverse flow | 0.82 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.65 | -- | % | ASTM D570 |
| Saturation 1 | 4.3 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 110 | -- | ASTM D785 | |
| Class r | 130 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 240 | 175 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 4.0 | % | ASTM D638 |
| Flexural Modulus | 13800 | 10500 | MPa | ASTM D790 |
| Flexural Strength | 305 | 260 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 170 | 190 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 260 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 255 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+9 | -- | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+12 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 35 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 290 | °C | |
| Front Temperature | 290 - 300 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4950E | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Medalist™ MD-12150 XRD (PRELIMINARY DATA) | Teknor Apex Company | TPE | Medalist™ |
| Badamid® C70 | Bada AG | Nylon 66/6 | Badamid® |
| ColorRx® TPE-OM50A0RXTP | LTL Color Compounders, Inc. | TPE | ColorRx® |
| OnForce™ LFT LFT PP-30 LGF/000 1001 | PolyOne Corporation | PP Homopolymer | OnForce™ LFT |