Tenac™ 7050
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wyoqqH_Tenac-7050.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™ 7050 is an Acetal (POM) Homopolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ 7050 include automotive, engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 34 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.7 to 2.1 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 94 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 73.0 | MPa | ISO 527-2 |
| -- | 75.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 111 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 13.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 56 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 172 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 136 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Specific Heat | 1470 | J/kg/°C | |
| Thermal Conductivity | 0.23 | W/m/K |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 1018 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| Sylvin 8992-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Karina GREEN COLOR CONCENTRATE 40/130-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MARPOL® LL6R 804UV | Marco Polo International, Inc. | mLLDPE | MARPOL® |
| Daelim Po1y® EP2001 | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |