LEXAN™ FXG154 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wyBtgg_LEXAN-FXG154-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FXG154 is a LEXAN PC grade with the Diamond effect. Color Package may affect properties, Application testing always recommended. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/3.8 kg) | 2.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 2.40 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.15 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.090 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2680 | MPa | ASTM D638 |
| -- | 2430 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 58.0 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 57.0 | MPa | ASTM D638 |
| Fracture | 54.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.9 | % | ASTM D638 |
| Yield | 6.2 | % | ISO 527-2/5 |
| Fracture 5 | 39 | % | ASTM D638 |
| Fracture | 75 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2390 | MPa | ASTM D790 |
| -- 7 | 2340 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 94.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 98.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 58 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 140 | J/m | ASTM D256 |
| 23°C | 750 | J/m | ASTM D256 |
| -30°C 10 | 16 | kJ/m² | ISO 180/1A |
| 23°C 11 | 51 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 62.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 133 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 129 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ASTM D1525 13 |
| -- | 147 | °C | ISO 306/B50 |
| -- | 149 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 260 - 291 | °C | |
| Cylinder Zone 2 Temp. | 260 - 291 | °C | |
| Cylinder Zone 3 Temp. | 260 - 291 | °C | |
| Cylinder Zone 4 Temp. | 260 - 291 | °C | |
| Cylinder Zone 5 Temp. | 260 - 291 | °C | |
| Adapter Temperature | 260 - 291 | °C |
| Extrusion instructions |
|---|
| Melt Temperature (Parison): 266 - 279 °CMinimum Moisture Content: 0.01 %Mold Temperature: 60 - 99 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemical Resources HD40948 | Chemical Resources, Inc. | HDPE | Chemical Resources |
| ECOLEN® HZ40S | HELLENIC PETROLEUM S.A. | PP Homopolymer | ECOLEN® |
| KRATON® D1102 E | Kraton Polymers LLC | SBS | KRATON® |
| Hyundai EP PPF HT940 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| Durethan® BKV 140 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |