Rotec® ASA E 610
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Rotec® ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wwcSAm_RotecASAE610.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rotec®ASA E 610 is an acrylonitrile-styrene-acrylate (ASA) material,. This product is available in Europe and is processed by extrusion or injection molding. Rotec®The main features of ASA E 610 are:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.30 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1800 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 36.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 25 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1800 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 54.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom 2946-96A | Spartech Polycom | PVC, Unspecified | Spartech |
| Taitalac® 8540T | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| Badamid® B70 GK30 FR HF | Bada AG | Nylon 6 | Badamid® |
| LG ASA LI923 | LG Chem Ltd. | ASA | LG ASA |
| POTICON RT8 | Otsuka Chemical Co., Ltd. | PPS | POTICON |