DOW™ VLDPE GRSN-1539 NT 7

Category:	VLDPE , Very Low Density Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ VLDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	wtg3XH_DOW-VLDPE-GRSN-1539-NT-7.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Low modulus film Excellent compatibility with polypropylene and polyethylene Granular form of FLEXOMER DFDA-1010 NT 7 VLDPE Resin Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a Consult the regulations for complete details. GRSN-1539 NT 7 Very Low Density Polyethylene VLDPE Resin is produced via gas phase polymerization from Dow. This is an ethylene-butene copolymer exhibiting high flexibility and elasticity. It can be utilized in monolayer and coextruded films and in blends with other polyolefins to enhance toughness of the structure. Granular form enhances rapid melt blending into polypropylene or polyethylene.

Message

Low modulus film

Excellent compatibility with polypropylene and polyethylene

Granular form of FLEXOMER DFDA-1010 NT 7 VLDPE Resin

Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a

Consult the regulations for complete details.

GRSN-1539 NT 7 Very Low Density Polyethylene VLDPE Resin is produced via gas phase polymerization from Dow. This is an ethylene-butene copolymer exhibiting high flexibility and elasticity. It can be utilized in monolayer and coextruded films and in blends with other polyolefins to enhance toughness of the structure. Granular form enhances rapid melt blending into polypropylene or polyethylene.

General Information
Agency Ratings	FDA 21 CFR 177.1520(c) 3.1a
Forms	Particles

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.905	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)			ASTM D1238
190°C/2.16 kg	0.85	g/10 min	ASTM D1238
190°C/21.6 kg	24	g/10 min	ASTM D1238

Hardness	Nominal Value	Test Method
Durometer Hardness		ASTM D2240
Shaw A, 1 sec	91	ASTM D2240
Shaw A, 5 seconds	94	ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	16.5	MPa	ASTM D638
Tensile Elongation (Break)	700	%	ASTM D638
Flexural Modulus - 2% Secant	152	MPa	ASTM D790A

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	-42.2	°C	Internal method
Melting Temperature (DSC)	119	°C	Internal method

Additional Information
根据 ASTM D 4976 进行基板模制和测试。

Resin Grade	Manufacturer	Category	Trademark
Zhongfa PP pp1	Yuyao Zhongfa Engineering Plastics Co. Ltd.	PP, Unspecified	Zhongfa
Axiall PVC 6850	Axiall Corporation	PVC, Flexible	Axiall PVC
KOCETAL® LW701	Kolon Plastics, Inc.	Acetal (POM) Copolymer	KOCETAL®
ImerPlast™ 10WPC	Imerys Minerals	Polyolefin, Unspecified	ImerPlast™
Karina WHITE PVC COMPOUND -E 838-10/182-Y-ERYB	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina