AIE PA6 50G6F
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | AIE PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wswbVV_AIE-PA6-50G6F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AIE PA6 50G6F is a polyamide 6 (nylon 6) material, which contains a filler of 30% glass fabric reinforcement. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of AIE PA6 50G6F are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 - 0.60 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 1.6 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2 |
| Flexural Modulus | 8100 | MPa | ISO 178 |
| Flexural Stress | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 207 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 220 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 225 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 245 - 260 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Mold Temperature | 50.0 - 110 | °C | |
| Injection Pressure | 30.0 - 80.0 | MPa | |
| Holding Pressure | 40.0 - 50.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Cylinder Temperature 4: 230 to 245°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8697-82 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ELASTOSIL® LR 3844/50 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Grilon® TSM-40/4 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| Karina WHITE PVC COMPOUND -E 839-10/ 68-Y-CRA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 6920X08 Brown 7474 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |