TECHNIACE® H-261
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Nippon A&L Inc. |
| Trademark: | TECHNIACE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ws8s1G_TECHNIACE-H-261.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNIACE® H-261 is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific or North America for injection molding. Primary attribute of TECHNIACE® H-261: Heat Resistant. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 53.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2350 | MPa | ISO 178 |
| Flexural Stress (23°C) | 87.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 43 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 103 | °C | ISO 75-2/A |
| CLTE - Flow (23 to 80°C) | 7.8E-5 | cm/cm/°C | JIS K7197 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 to 115 | °C | |
| Drying Time | > 3.0 | hr | |
| Rear Temperature | 240 to 280 | °C | |
| Middle Temperature | 240 to 280 | °C | |
| Front Temperature | 240 to 280 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ HDPE LP 8000 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| KOPA® KN136 | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| LNP™ LUBRILOY™ D2000AXH compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |
| OPNYL OP66GF50 | Ovation Polymers Inc. | Nylon 66 | OPNYL |
| Dryflex® V 85A101 | ELASTO | TPV | Dryflex® |