Lumid® GN1001AF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wrzkxf_Lumid-GN1001AF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Halogen Free Flame Retardant Applications Electrical & Electronic(Switch) |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C, 3.20 mm) | 1.0 to 1.4 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 76.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 15 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 3140 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 190 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 60.0 | °C | |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 3.00 | ASTM D150 | |
| Arc Resistance | 80.0 | sec | ASTM D495 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 225 to 245 | °C | |
| Middle Temperature | 230 to 260 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure 5 | 0.490 to 1.96 | MPa | |
| Screw Speed | 60 to 200 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Hydraulic Type |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Zythane® 5050D | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| Durethan® C 38 FKS 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| DURANEX® 330LC | Polyplastics Co., Ltd. | PBT | DURANEX® |
| PAXOTHENE® NA205-15 | USI Corporation | LDPE | PAXOTHENE® |