Adsyl 3 C 30 F HP
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adsyl |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wrMx4u_Adsyl-3-C-30-F-HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adsyl 3 C 30 F HP is an advanced polyolefin, specially designed for use as a sealing or metallized layer in co-extruded film applications. This grade features a low seal initiation temperature, a high melting point and good optics. It does not contain slip or anti-block additives. For regulatory information please refer to Adsyl 3 C 30 F HP Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.5 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus 1 | ASTM D882 | ||
| MD : 50 µm, Cast Film | 400 | MPa | |
| TD : 50 µm, Cast Film | 400 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield, 50 µm, Cast Film | 18.0 | MPa | |
| TD : Yield, 50 µm, Cast Film | 18.0 | MPa | |
| MD : Break, 50 µm, Cast Film | 44.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 38.0 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Yield, 50 µm, Cast Film | 12 | % | |
| TD : Yield, 50 µm, Cast Film | 10 | % | |
| MD : Break, 50 µm | 850 | % | |
| TD : Break, 50 µm, Cast Film | 850 | % | |
| Seal Initiation Temperature | 112 | °C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 71.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 122 | °C | ISO 306/A50 |
| Melting Temperature | 137 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 91 | ASTM D2457 | |
| Haze (50.0 µm) | 0.40 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4085 TFE 13 SI 2 | RTP Company | PPA | RTP |
| Tislamid® PA66 PA66 25 GBR | Tisan | Nylon 66 | Tislamid® PA66 |
| TPUCO® TPUI-E85 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Chemiton HHF0NA 50 | Franplast S.r.l. | SEBS | Chemiton |
| Karina BLACK PVC COMPOUND 950-48/4-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |