ALCOM® PA66 910/32.1 GF8 TCE8
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wrGwyA_ALCOM-PA66-910-32-1-GF8-TCE8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM® PA66 910/32.1 GF8 TCE8 is a Polyamide 66 (Nylon 66) product filled with 8.0% filler and 8.0% glass fiber. It is available in Asia Pacific, Europe, or North America. Applications of ALCOM® PA66 910/32.1 GF8 TCE8 include automotive, electrical/electronic applications, engineering/industrial parts, housings and lighting applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.51 | -- | g/cm³ | ISO 1183 |
| Spiral Flow 1 | 25.0 | -- | cm | |
| Molding Shrinkage (24 hr) | 0.60 | -- | % | ISO 294-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 142 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10400 | -- | MPa | ISO 527-2 |
| Tensile Stress | 52.0 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.0 | -- | % | ISO 527-2 |
| Flexural Modulus | 11700 | -- | MPa | ISO 178 |
| Flexural Stress | 88.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 6.0 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 246 | -- | °C | ISO 306/B50 |
| Thermal Conductivity | ||||
| -- 2 | 3.5 | -- | W/m/K | ASTM E1461 |
| -- 3 | 16 | -- | W/m/K | ASTM E1461 |
| -- 4 | 8.0 | -- | W/m/K | ISO 22007-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.5E+2 | ohms | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 12 | hr | |
| Processing (Melt) Temp | 300 to 320 | °C | |
| Mold Temperature | > 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2 mm |
| 2 . | through-plane |
| 3 . | in-plane |
| 4 . | integral |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPC PVC SM66E | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| 3M™ Dyneon™ Fluoroplastic FEP 6301Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| Anjacom® R050/65S | Almaak International GmbH | PC+ABS | Anjacom® |
| Ecomass® 3800ZD82 | Ecomass Technologies | PMP | Ecomass® |
| Hostacom TYC727D | LyondellBasell Industries | TPO (POE) | Hostacom |