Geon™ Vinyl Rigid Molding MP402
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Rigid Molding |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wqXioD_Geon-Vinyl-Rigid-Molding-MP402.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| *UL VO and 5VA values are associated with Trans colors only. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Spiral Flow | 81.3 | cm | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 83 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2620 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 47.6 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 35 | % | ASTM D638 |
| Flexural Modulus | 2480 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| 0°C, 3.18 mm, Injection Molded | 110 | J/m | |
| 23°C, 3.18 mm, Injection Molded | 800 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 67.2 | °C | |
| 0.45 MPa, Annealed, 6.35 mm | 71.1 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 67.2 | °C | |
| 1.8 MPa, Annealed, 6.35 mm | 70.0 | °C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.19 mm, ALL | V-0 | ||
| 1.47 mm, ALL | 5VA |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 4(3180 µm) | 76.0 | % | ASTM D1003 |
| Haze (3180 µm) | 7.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 199 to 204 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | CIE Illuminant C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoprene® T60K4 NERO900 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| WELLAMID Nylon 6600 GV 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Celstran® PP-GF40-0405 P10/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Dynaprene® 1065A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Petrothene® LT493701 | LyondellBasell Industries | HDPE, UHMW | Petrothene® |