Radilon® A RV500K 990 GRI
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wqK52h_Radilon-A-RV500K-990-GRI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 50% glass fiber reinforced injection moulding grade, low friction. Heat stabilized. Natural grey colour. Suitable for parts requiring low friction, very high stiffness and high mechanical resistance. Good resistance to heat ageing. ISO 1043 : PA66-T GF50 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.59 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 4.6 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17300 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 220 | -- | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.8 | -- | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 16600 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 350 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (-30°C) | 12 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 85 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 250 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 290 to 305 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 FR MS 5 | RTP Company | Nylon 66 | RTP |
| TES J-1200/40 | Techmer Engineered Solutions | ABS | TES |
| UmaPET WH | Ester Industries Ltd. | PET | UmaPET |
| GPPC PS-302 | GPPC Chemical Co., Ltd. | PS (HIPS) | GPPC |
| Hostacom ETA5081 | LyondellBasell Industries | TPO (POE) | Hostacom |