CYCOLOY™ RCX7233 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wpzZQN_CYCOLOY-RCX7233-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLOY RCX7233 (experimental grade name EXCY0355) resin is an injection moldable impact modified PC blend with non-brominated and non-chlorinated flame retardant. It contains 30% post consumer recycle content with a UL-94 V0 rating @ 0.75 mm for all color. Developed for applications require excellent flow and impact balance with thin wall flame resistance. Limited availability and restricted color only. |
| General Information | |
|---|---|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2500 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 60.0 | MPa | |
| Break | 55.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 4.0 | % | |
| Break | 60 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2400 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -30°C | 130 | J/m | ASTM D256 |
| 23°C | 690 | J/m | ASTM D256 |
| 23°C 6 | 50 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 57.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 103 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 87.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 93.0 | °C | |
| Vicat Softening Temperature | 107 | °C | ASTM D1525 7 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm, Testing by SABIC | V-2 | ||
| 0.750 mm, Testing by SABIC | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 230 to 280 | °C | |
| Middle Temperature | 240 to 290 | °C | |
| Front Temperature | 250 to 300 | °C | |
| Nozzle Temperature | 250 to 300 | °C | |
| Processing (Melt) Temp | 250 to 300 | °C | |
| Mold Temperature | 60.0 to 85.0 | °C | |
| Vent Depth | 0.030 to 0.075 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*3 |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 128 HF | RTP Company | PP Homopolymer | RTP |
| Sinvicomp SRF3704UV | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TIPPLEN® R 359 | MOL Petrochemicals Co. Ltd. | PP Random Copolymer | TIPPLEN® |
| EpoxAcast® 690 | Smooth-On, Inc | Epoxy | EpoxAcast® |
| Sylvin 5143-88 White 1554 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |