Adell Polyamide AR-38
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Adell Plastics, Inc. |
| Trademark: | Adell Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wnbmVG_Adell-Polyamide-AR-38.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adell Polyamide AR-38 is a polyamide 66 (nylon 66) material, which contains a 40% glass fiber reinforced material. This product is available in North America,. The typical application field of Adell Polyamide AR-38 is: automobile industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 101 | ASTM D785 | |
| Class r | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 221 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 290 | MPa | ASTM D790 |
| Compressive Strength | 276 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 249 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 249 | °C | ASTM D648 |
| Melting Temperature | 254 - 271 | °C |
| Additional Information |
|---|
| DTUL @ 264 psi, ASTM D648: >480°FDTUL @ 66 psi, ASTM D648: >480°FElongation at Break, ASTM D638: 3 to 4%Specific Gravity, ASTM D792: 1.38 to 1.4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7610 H | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Ateva® 1641 | Celanese EVA Performance Polymers | EVA | Ateva® |
| HYPERTHERM™ 2399 NT | The Dow Chemical Company | HDPE | HYPERTHERM™ |
| Panlite® B-8110R | TEIJIN LIMITED | PC | Panlite® |
| ULTEM™ CRS5201R resin | SABIC Innovative Plastics | PEI | ULTEM™ |