SABIC® HDPE FI0750
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wlrFQZ_SABIC-HDPE-FI0750.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE FI0750 is a high molecular high density polyethylene copolymer grade typically used for blown film applications. SABIC® HDPE FI0750 features are balance between toughness and stiffness, good impact properties with low gel level. Typical applications SABIC® HDPE FI0750 is typically used for blown film extrusion. Typical applications are heavy duty bags, grocery sacks, shopping bags, refuse bags, liners for multi-wall sacks and liners for frozen food meat. The grade can be blended with LLDPE and LDPE and can be used in co-extrusion process. Processing conditions Melt Temperature: 200-225°C Frost Line Height: 6-8 times die cross-cut BUR: 3-5 Film properties Film properties have been measured at 20 µm blown film with a BUR = 4. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 7.5 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.22 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 61 | ISO 868 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm | 50.0 | MPa | ISO 527-3 |
| TD : Yield, 20 µm | 45.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 20 µm | 400 | % | ISO 527-3 |
| TD : Break, 20 µm | 450 | % | ISO 527-3 |
| Dart Drop Impact 1(20 µm) | 250 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 74.0 | °C | ISO 306/B |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 6383-2 | ||
| MD : 20.0 µm | 200.0 | kN/m | ISO 6383-2 |
| TD : 20.0 µm | 425.0 | kN/m | ISO 6383-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 225 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 2636 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Badamid® LB70 GF/M40 | Bada AG | Nylon 6 | Badamid® |
| Colorite 12 Series 5012 | Colorite Polymers | PVC, Unspecified | Colorite 12 Series |
| Hifax HSBM CB 1157 BLACK | LyondellBasell Industries | PP Copolymer | Hifax |
| 3M™ Dyneon™ Fluoroelastomer FE 5625N | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |