CYCOLAC™ DL100 resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wlfc28_CYCOLAC-DL100-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLAC DL100 is a high heat, high impact, low emissions ABS/PC blend. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 to 0.70 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 91.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 46.0 | MPa | ISO 527-2/5 |
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 3.5 | % | ISO 527-2/5 |
| Yield | 3.4 | % | ISO 527-2/50 |
| Break | 60 | % | ISO 527-2/5 |
| Break | 10 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2260 | MPa | ISO 178 |
| Flexural Stress | 69.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 34 | kJ/m² | |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 35 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 104 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 87.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/B50 |
| -- | 107 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 9.8E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 9.8E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 250 to 280 | °C | |
| Front Temperature | 250 to 280 | °C | |
| Nozzle Temperature | 245 to 275 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A GF 30 HR | A. Schulman Europe | PBT | SCHULADUR® |
| Sylvin 9708-80C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Zhongfa PP DD2 1x102 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Niche PPHG30BK | Niche Polymer, LLC | PP Homopolymer | Niche |
| EPAMOULD 685A56 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |