POCAN® S 7926 000000

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	LANXESS GmbH
Trademark:	POCAN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	wlN3Cw_POCANS7926000000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PBT, non-reinforced, injection molding,Extrusion, flame retardant, improved impact strength

General Information
Features	Impact resistance, good Flame retardancy
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Extrusion Injection molding
Multi-Point Data	Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.37	g/cm³	ISO 1183
Apparent Density	0.80	g/cm³	ISO 60
Melt Volume-Flow Rate (MVR) (270°C/5.0 kg)	40.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Vertical flow direction : 250°C, 2.00mm ¹	2.0	%	ISO 294-4
Vertical flow direction : 120°C, 2 hours, 2.00mm ²	0.30	%	ISO 294-4
Flow direction : 250°C, 2.00mm ³	2.1	%	ISO 294-4
Flow direction : 120°C, 2 hours, 2.00mm ⁴	0.30	%	ISO 294-4
Water Absorption			ISO 62
Saturated, 23°C	0.40	%	ISO 62
Equilibrium, 23°C, 50% RH	0.20	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	120	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2400	MPa	ISO 527-2/1
Tensile Stress (Yield, 23°C)	40.0	MPa	ISO 527-2/50
Tensile Strain (Yield, 23°C)	3.0	%	ISO 527-2/50
Nominal Tensile Strain at Break (23°C)	> 10	%	ISO 527-2/50
Tensile Creep Modulus			ISO 899-1
1 hr	2300	MPa	ISO 899-1
1000 hr	1500	MPa	ISO 899-1
Flexural Modulus ⁵(23°C)	2300	MPa	ISO 178/A
Flexural Stress ⁶
3.5% strain	65.0	MPa	ISO 178/A
23°C	70.0	MPa	ISO 178
Flexural Strain at Flexural Strength (23°C) ⁷	5.0	%

Thermal	Nominal Value	Unit	Test Method
Halving Interval			IEC 60216
-- ⁸	5.5	°C	IEC 60216
-- ⁹	13.0	°C	IEC 60216
-- ¹⁰	13.0	°C	IEC 60216
Temperature index ¹¹			IEC 60216
Electric Strength	140		IEC 60216
Tensile Impact Strength	110		IEC 60216
Tensile Strength	140		IEC 60216

Additional Information	Nominal Value		Test Method
Electrolytical Corrosion	A 1		IEC 60426
ISO Shortname	PBT, GFHMPR, 11-020; ISO 1043-PBT FR (17)		ISO 7792

Injection	Nominal Value	Unit	Test Method
Residual Moisture Content	0.0 - 0.020	%	Karl Fisher

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	< 10	kJ/m²	ISO 179/1eA
23°C	12	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	No Break		ISO 179/1eU
23°C	No Break		ISO 179/1eU
Notched Izod Impact			ISO 180/1A
-40°C	< 10	kJ/m²	ISO 180/1A
-30°C	< 10	kJ/m²	ISO 180/1A
23°C	< 10	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength			ISO 180/1U
-30°C	110	kJ/m²	ISO 180/1U
23°C	No Break		ISO 180/1U
Multi-Axial Instrumented Impact Peak Force (23°C)	80.0	N	ISO 6603-2

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	130	°C	ISO 75-2/B
1.8 MPa, not annealed	60.0	°C	ISO 75-2/A
8.0 MPa, not annealed	47.0	°C	ISO 75-2/C
Vicat Softening Temperature	160	°C	ISO 306/B120
Ball Pressure Test (190°C)	Pass		IEC 60695-10-2
Melting Temperature ¹²	225	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : 23 to 55°C	1.1E-4	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	1.2E-4	cm/cm/°C	ISO 11359-2
Thermal Conductivity (23°C)	0.25	W/m/K	ISO 8302
RTI Elec	125	°C	UL 746
RTI Imp	110	°C	UL 746
RTI	125	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity (23°C)	> 1.0E+15	ohms·cm	IEC 60093
Dielectric Strength (23°C, 1.00 mm)	30	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 100 Hz	3.20		IEC 60250
23°C, 1 MHz	3.10		IEC 60250
Dissipation Factor			IEC 60250
23°C, 100 Hz	1.5E-3		IEC 60250
23°C, 1 MHz	0.015		IEC 60250
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.400 mm)	V-0		UL 94
Glow Wire Flammability Index (0.800 mm)	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature			IEC 60695-2-13
0.800 mm	700	°C	IEC 60695-2-13
1.60 mm	700	°C	IEC 60695-2-13
3.00 mm	700	°C	IEC 60695-2-13
Oxygen Index ¹³	30	%	ISO 4589-2

Injection	Nominal Value	Unit	Test Method
Drying Temperature - Circulation Dryer	120	°C
Drying Time - Circulation Dryer	4.0 - 8.0	hr
Processing (Melt) Temp	240 - 260	°C
Mold Temperature	80.0 - 100	°C

Note Message
1 .	60x60x2; WZ 80°C; 600 Bar
2 .	60x60x2
3 .	60x60x2; WZ 80°C; 600 Bar
4 .	60x60x2
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	Pull Rate: 2 mm/min; 50% RH
8 .	Tensile Impact Strength
9 .	Electric Strength
10 .	Tensile Strength
11 .	20000 h
12 .	10°C/min
13 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
Victron® 095G4	Asia International Enterprise (Hong Kong) Limited	PEEK	Victron®
APEX® 85-J644Z-3	Teknor Apex Company	PVC, Flexible	APEX®
ASTATAL™ FV30	Marplex Australia Pty. Ltd.	Acetal (POM) Homopolymer	ASTATAL™
LEXAN™ LUX9612G resin	SABIC Innovative Plastics Europe	PC	LEXAN™
POLYFLON™ D-6B	DAIKIN AMERICA, INC.	PTFE	POLYFLON™