Lotader® HX8290
| Category: | EAA , Ethylene Acrylic Acid Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotader® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wkctb9_Lotader-HX8290.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTADER® HX8290 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process. Applications Due to its properties, reactivity, fluidity and compatibility with tackifying resins and waxes, LOTADER ® HX8290 is suitable as additive for hot melt adhesive formulations and as coupling agent in mineral filled compounds such as halogen free flame retardant wires and cables. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 70 | g/10 min | ASTM D1238, ISO 1133 |
| Ethyl Acrylate Content | 17.0 | wt% | |
| Maleic Anhydride Content | 2.8 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 6.00 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 700 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (Compression Molded) | 30.0 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | < 40.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 85.0 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T10P250-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| TATREN® IM 25 75 | Slovnaft Petrochemicals, s.r.o. | PP Impact Copolymer | TATREN® |
| TRIMID® N66-100NL | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| LOTTMER HX-145DB | Lotte Chemical Corporation | TPE | LOTTMER |
| Neoflex™ 8140 | Zylog Plastalloys Pvt. Ltd. | TPE | Neoflex™ |