CERTENE™ LLHF-117XA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wkEBbE_CERTENE-LLHF-117XA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLHF-117XA is a certified prime grade Ethylene-Hexene Copolymer specially developed for extrusion of SUPER STRENGTH Blown films of outstanding Impact and Toughness. LLHF-117XA features good processability and films exhibit exceptional Elmendorf Tear strength and Puncture resistance. LLHF-117XA major applications include super strong liners, lamination films, stretch wrapping films, and super strong carry-on-bags. Maximum recommended film drawdown is 0.3 mil. LLHF-117XA contains no slip and no antiblock. LLHF-117XA complies with FDA regulation 21CFR 177.1520 (c) 3.2(a) and most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.917 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 193 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 207 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 11.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 12.0 | MPa | ASTM D882 |
| MD : Break, 25 µm | 55.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 40.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 650 | % | ASTM D882 |
| TD : Break, 25 µm | 780 | % | ASTM D882 |
| Dart Drop Impact 1(25 µm) | 480 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 430 | g | ASTM D1922 |
| TD : 25 µm | 750 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 9.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.0 mils (25 µm) film, melt temperature 420-450°F (215-230°C), blow-up-ratio 2.5 :1. |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G25 291 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Tecoform® PO20 NL IL | Eurotec Engineering Plastics | Acetal (POM) Copolymer | Tecoform® |
| Celcon® GC10 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| HyTemp® AR12 | Zeon Chemicals L.P. | Acrylic, Unspecified | HyTemp® |
| Optix® CA-82 UVA | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |